Toluene → Ethylene 5-norbornen-2-ol

Temperature

20 °C

A glass reactor was loaded inside a glove box with L(iPr2)Ni(ηl-CH2Ph)(PMe3) (about 20 μmol; 2.00 g of 8.77 mM solution in toluene), Ni(COD)2 (about 50 μmol; 2.50 g of 17.6 mM solution in toluene), 5-Norbornen-2-ol (about 3.99 mmol; 3.00 g of 1.15 M solution in toluene) and toluene (about 18.45 g) such that the total volume of the toluene solution was about 30 mL. The glass reactor was scaled inside the glove box and was attached to a vacuum/nitrogen line manifold. Ethylene was fed continuously into the reactor at about 100 psi and the pressurized reaction mixture was stirred at about 20° C. Ethylene was vented after about 20 minutes and acetone was added to quench the polymerization. The precipitated polymer was collected by filtration and dried under high vacuum overnight. The reaction produced about 0.619 g of ethylene/5-norbornen-2-ol co-polymer. The activity of the catalyst with respect to ethylene consumption was about 118 kg mol−1 h−1.

1. customto quench
2. customthe polymerization
3. filtrationThe precipitated polymer was collected by filtration
4. customdried under high vacuum overnight

ORD record

ord-1383596a554b482e82d3e763d81a965d

Source dataset

uspto-grants-2007_08

DOI

10.6084/m9.figshare.5104873.v1

Patent number

US07259214B2