反应详情

11.4 g of sodium nitrite, 28.0 g of sulfanilic acid and 1200 g of 0° C. water were fed into a reactor to form diazonium sulfanilate, to which was added 200 g of a carbon black pigment, Raven C. When the generation of nitrogen ceased, the reaction mixture was concentrated, and further reacted at an elevated temperature. The resulting mixture was extracted with ethanol for 12 hours in a Soxhlet's extractor to remove unreacted compounds and side products, and this was again dissolved in water and filtered to obtain a dispersion of about 20 wt. % sulfanilate-processed carbon black pigment. On the other hand, 3.6 g of aminostyrene, 2.1 g of sodium nitrite and 150 g of water were fed into a separate reactor to form a diazonium salt of 4-aminostyrene, and this was dissolved in 10 g of ethanol. The sulfanilate-processed carbon black pigment dispersion was added to the diazonium salt solution and reacted for 18 hours with stirring. Then, this was filtered and purified through Soxhlet extraction to obtain a dispersion of a carbon black pigment having 4-aminostyrene added to its surface. Next, 30 g of deionized water was degassed in a nitrogen atmosphere at 90° C. in a reactor, and a mixture of 28.13 g of the 4-aminostyrene-added carbon black pigment dispersion, 2.0 g of methyl methacrylate, 2.0 g of butyl acrylate, and 1.0 g of polyethylene glycol 2000 monomethyl ether acrylate dissolved in 3.0 g of deionized water was dropwise added thereto over a period of 20 minutes. 0.22 g of potassium persulfate was added thereto and reacted at 80° C. for 18 hours. The resulting product was concentrated under reduced pressure, and extracted with acetone in an Soxhlet's extractor to remove the non-added polymer. The process gave an intended dispersion of a pigment having a polymer group bonded to its surface.