Reaktionsgleichung
[B:1]([OH:4])([OH:3])[OH:2].[N:5]1[C:12]([NH2:13])=[N:11][C:9]([NH2:10])=[N:8][C:6]=1[NH2:7].C(=O)([O-])[O-].[Ca+2]>>[B:1]([OH:4])([OH:3])[OH:2].[N:5]1[C:12]([NH2:13])=[N:11][C:9]([NH2:10])=[N:8][C:6]=1[NH2:7]Komponenten
4
Versuchsvorschrift
First, 70 kg of orthoboric acid, 50 kg of melamine, and 1 kg of calcium carbonate were mixed by a Henschel mixer. Next, the mixture was placed in a constant temperature and humidity chamber at a temperature of 80° C. and a relative humidity of 80% for 2 hours to produce melamine borate. Then, the melamine borate was subjected to calcination and crystallization in a batch atmosphere furnace under a nitrogen atmosphere at 1750° C. for 2 hours to yield boron nitride with a graphitization index (GI) of 3.95 and a specific gravity of 2.27 g/cm3. After that, grinding was adjusted to prepare D-6 with a volume-average particle diameter of 18.0 μm.
Aufarbeitung
- customwas placed in a constant temperature and humidity chamber at a temperature of 80° C.
Quellen und Nachweise
- ORD-Eintrag
- ord-befd201c3ed0481bac2f6a7af77149bc
- Quelldatensatz
- uspto-grants-2013_10
- Patentnummer
- US08557905B2