Sodium aluminate → Sodium aluminosilicate

Temperatur

100 °C

0.723 g of sodium hydrate (97%) was dissolved in 80 ml of distilled water, and then it was divided into two Teflon reaction containers in halves for each. In one container it was dissolved by adding 8.258 g of sodium aluminate, and in the other container it was dissolved by adding 15.48 g of sodium meta-silicate. Subsequently, gel was formed as a result of adding the silicate solution to the aluminate solution quickly. It was stirred until gel became completely dissolved and then heated at 100° C. for 4 days to obtain zeolite A having Si/Al ratio 1.020 containing impurities. The obtained catalyst was cleaned several times with distilled water and then dried inside an oven at 100° C., and then had a reflux using aqueous solution having 0.1M of ammonium nitrate per 1 g of the catalyst to remove Na ion, which was contained in the catalyst. After this process, the catalyst was cleaned several times with distilled water and dried inside an oven, and then calcined more for 4 hours in the air at 500° C. to obtain pure zeolite A having Si/Al ratio 1.020.

1. dissolutionIn one container it was dissolved
2. dissolutionin the other container it was dissolved
3. customSubsequently, gel was formed as
4. customa result
5. dissolutionbecame completely dissolved

ORD-Eintrag

ord-03141f8e27bc48a3b79cd8987148129e

Quelldatensatz

uspto-grants-2007_04

DOI

10.6084/m9.figshare.5104873.v1

Patentnummer

US07202376B2