[OH:1][C:2]1[CH:3]=[C:4]([N:8]2[C:12](=[O:13])[CH:11]=[CH:10][C:9]2=[O:14])[CH:5]=[CH:6][CH:7]=1.[N:15]#[C:16]Br.CC(C)=O.C(N(CC)CC)C>O>[O:13]=[C:12]1[CH:11]=[CH:10][C:9](=[O:14])[N:8]1[C:4]1[CH:3]=[C:2]([O:1][C:16]#[N:15])[CH:7]=[CH:6][CH:5]=1
A 15.80 gram portion of N-(3-hydroxyphenyl)maleimide (0.0835 mole), 9.29 grams of cyanogen bromide (0.0877 mole) and 300 milliliters of acetone were added to a reactor and maintained under a nitrogen atmosphere with stirring. The stirred solution was cooled to -5° C. then 8.50 grams of triethylamine (0.0840 mole) was added to the reactor over a ten minute (600 s) period and so as to maintain the reaction temperature at -5° to -3° C. After completion of the triethylamine addition, the reactor was maintained at -5° to -3° C. for an additional forty minutes (2400 s), followed by addition of the reactor contents to 1500 milliliters of deionized water. After five minutes (300 s), the water and product mixture was multiply extracted with three 100 milliliter volumes of methylene chloride. The combined methylene chloride extract was washed with 1000 milliliters of deionized water followed by a second deionized water washing with 500 milliliters of deionized water then drying over anhydrous sodium sulfate. The dry methylene chloride extract was filtered and solvent removed by rotary evaporation under vacuum for 30 minutes at 100° C. 3-(2,5-dihydro-2,5-dioxo-1H-pyrrol-1-yl)phenyl cyanate (16.2 grams) was recovered in 90.6 percent yield as a light tan colored powder. Infrared spectrophotometric analysis of a film sample of the product confirmed the product structure (disappearance of phenolic hydroxyl absorbance, appearance of cyanate absorbance at 2232 and 2274 cm-1, maintenance of maleimide carbonyl absorbance at 1714 cm-1).
Wird geladen…