Reaktionsgleichung
[Ir:1].[Ta:2].C([OH:7])CCC>[Ti]>[Ir:1]=[O:7].[O-2:7].[Ta+5:2].[O-2:7].[O-2:7].[O-2:7].[O-2:7].[Ta+5:2]Komponenten
Edukt 3
Produkt 1
Reagenzien, Katalysatoren, Lösungsmittel 1
Versuchsvorschrift
After the roughened titanium substrate surface was heat treated, it was painted with a n-butanol solution containing salts of iridium and tantalum. The ratio of iridium to tantalum in the solution was about 65% to 35% by weight. The solution was allowed to dry at ambient temperature for approximately 20 minutes. The painted titanium substrate was subsequently heat treated in a furnace having an oxygen containing atmosphere at approximately 500° C. for approximately 20-30 minutes to form an iridium oxide/tantalum oxide composite coating. The process of painting and heat treating the titanium substrate was repeated to obtain a first layer having a total loading of 2.0 g/m2. After the desired loading was achieved, the anode was heat treated for approximately one hour at approximately 500° C.
Aufarbeitung
- additiontreated
- customto dry at ambient temperature for approximately 20 minutes
- temperatureThe painted titanium substrate was subsequently heat
- additiontreated in a furnace
- customat approximately 500° C.
- customfor approximately 20-30 minutes
Quellen und Nachweise
- ORD-Eintrag
- ord-c7848c10c67f4658b8f52f05a07d6b97
- Quelldatensatz
- uspto-grants-2001_04
- Patentnummer
- US06217729B1