Reaktionsgleichung
CC(C(OC)=O)=C.COCC(O)C.CC(=O)CC(C)(O)C.CCCCCCCCOC(CCC1C=C([N:41]2[N:49]=[C:48]3[C:43]([CH:44]=[CH:45][CH:46]=[CH:47]3)=[N:42]2)C(O)=C(C(C)(C)C)C=1)=O.CCC(C1C=C(N2N=C3C(C=CC=C3)=N2)C(O)=C(C(CC)(C)C)C=1)(C)C.CC(CC(C1C=CC(O)=C(N2N=C3C(C=CC=C3)=N2)C=1)(C)C)(C)C>>[NH:42]1[C:43]2[CH:44]=[CH:45][CH:46]=[CH:47][C:48]=2[N:49]=[N:41]1Komponenten
7
Versuchsvorschrift
A coating solution was prepared containing 7 grams (g) of Elvacite 2041 PMMA, 79 g of 1-methoxy-2-propanol, 14 g of diacetone alcohol, 0.85 g of Tinuvin 384, 0.43 g of Tinuvin 328, 0.22 g of Cyasorb 5411, and 2 drops of BYK 331 surfactant. Thus, the solution contains 7% PMMA by total weight and 10% Tinuvin 384, 5% Tinuvin 328, and 2.5% Cyasorb 5411 based on solids. This solution was applied by flow coating onto 7 mil (177.8 μm) polycarbonate films 10 inches (25.4 cm) wide and 15 inches (38.1 cm) long, the solvent was flashed at 50° C. for 10 minutes, and the coated film was baked for 1 hour at 100° C. The top 5 inches (12.7 cm) of the films was discarded.
Aufarbeitung
- customA coating solution was prepared
- waitthe coated film was baked for 1 hour at 100° C
Quellen und Nachweise
- ORD-Eintrag
- ord-f0f27b3d5f4445b495693b4ff407852b
- Quelldatensatz
- uspto-grants-2013_09
- Patentnummer
- US08525191B2
Verknüpfte Notizen
Wird geladen…