Hydrogen Peroxide → Disodium

HRID 43039

Reaktionsgleichung

Reaktionsgleichung von HRID 43039
C(O)(=O)C=C.SCCC(O)=O.[S:12]([O-:15])([O-:14])=[O:13].[Na+:16].[Na+:17].[Na][Na].[OH:20][CH:21](S([O-])=O)[C:22]([OH:24])=[O:23].OO.[OH-].[Na+]>O.O.O.O.O.O.O.O.S([O-])([O-])(=O)=O.[Fe+2]>[Na:16][Na:17].[OH:20][CH:21]([S:12]([O-:15])(=[O:14])=[O:13])[C:22]([OH:24])=[O:23]

Komponenten

12

Edukt 7

HCID 784Hydrogen PeroxideHCID 65143-Mercaptopropionic AcidHCID 6581Acrylic AcidHCID 14798Sodium HydroxideHCID 24437Sodium SulfiteHCID 141233DisodiumHCID 211332982-Hydroxy-2-sulfinatoacetic acid

Produkt 2

HCID 141233DisodiumHCID 1317308552-Hydroxy-2-sulphonatoacetic acid

Reagenzien, Katalysatoren, Lösungsmittel 3

HCID 962WaterKatalysatorHCID 62662Ferrous sulfate heptahydrateKatalysatorHCID 962WaterLösungsmittel3×

Versuchsvorschrift

A glass reactor equipped with several feeding devices, stirrer and pH electrode was charged with 382 g of water, 263 g of vinyloxybutylpolyethylene glycol-3000 (prepared by ethoxylation of hydroxybutyl vinyl ether with 66 mol EO) and 96 g of isoprenylpolyethylene glycol-1100 (prepared by ethoxylation of 3-methyl-3-buten-1-ol with 22 mol EO) (solution A) and was thermostated at 13° C. 35% of a second prepared, partly neutralized solution (solution B) consisting of 68 g of water and 63.6 g of acrylic acid (99%) was added to solution A over a period of 15 min in the glass reactor. Furthermore, 3.6 g of 3-mercaptopropionic acid were added to the reactor. A third solution (solution C) consisting of 10 g of a mixture of sodium sulphite, the disodium salt of 2-hydroxy-2-sulphinatoacetic acid and the disodium salt of 2-hydroxy-2-sulphonatoacetic acid (Brüggolit FF6 from Brüggemann GmbH) and 60 g of water was prepared. Thereafter, 50 mg of iron(II) sulphate heptahydrate, dissolved in a few drops of water, and 5 g of 50% strength hydrogen peroxide solution were added to solution A at a temperature of 13° C. At the same time, the still remaining solution B was dosed over 45 minutes and solution C over 60 minutes into the solution A. Finally, neutralization was effected with 20% strength sodium hydroxide solution. The aqueous solution of a copolymer having an average molecular weight of Mw=22 400 g/mol (determined by GPC) and a solids content of 41% was obtained.

Aufarbeitung

  1. customA glass reactor equipped
  2. customat 13° C
  3. customa solids content of 41% was obtained