Phenylphosphonic Acid → Zinc Oxide

HRID 576026

Reaktionsgleichung

Reaktionsgleichung von HRID 576026
[O-2].[Zn+2:2].[C:3]1([P:9](=[O:12])([OH:11])[OH:10])[CH:8]=[CH:7][CH:6]=[CH:5][CH:4]=1>O>[O-2:10].[Zn+2:2].[C:3]1([P:9](=[O:10])([O-:12])[O-:11])[CH:8]=[CH:7][CH:6]=[CH:5][CH:4]=1.[Zn+2:2]

Komponenten

5

Edukt 2

HCID 15295Phenylphosphonic AcidHCID 3007857Zinc Oxide

Produkt 2

HCID 3007857Zinc OxideHCID 15878909Phosphonic acid, P-phenyl-, zinc salt (1:1)

Reagenzien, Katalysatoren, Lösungsmittel 1

HCID 962WaterLösungsmittel2×

Versuchsvorschrift

An aqueous slurry of zinc oxide was prepared by charging a 300 mL reaction flask equipped with a stirrer with 10.0 g (123 mmol) of zinc oxide (JIS grade 2, available from HakusuiTech Ltd.) and 90.0 g of water. An aqueous solution of 13.6 g (86 mmol) of phenylphosphonic acid (available from Nissan Chemical Industries, Ltd.) dissolved in 77.0 g of water was gradually added dropwise at room temperature (about 25° C.) to this slurry with stirring, thereby effecting a reaction for one hour. The slurry was then filtered, and the wet cake was thoroughly rinsed with water. The wet cake was subsequently dried at 120° C. for at least 12 hours, yielding a white powder of zinc phenylphosphonate-containing zinc oxide.

Aufarbeitung

  1. customa 300 mL reaction flask
  2. additionwas gradually added dropwise at room temperature (about 25° C.) to this slurry
  3. customa reaction for one hour
  4. filtrationThe slurry was then filtered
  5. washthe wet cake was thoroughly rinsed with water
  6. customThe wet cake was subsequently dried at 120° C. for at least 12 hours