[C:1]([OH:6])(=[O:5])[C:2]([CH3:4])=[CH2:3].C1(N=C=NC2CCCCC2)CCCCC1.[CH2:22]([CH2:24][NH2:25])[OH:23]>>[C:1]([NH:25][CH2:24][CH2:22][OH:23])(=[O:6])[C:2]([CH3:4])=[CH2:3].[C:1]([O:6][CH2:24][CH2:22][OH:23])(=[O:5])[C:2]([CH3:4])=[CH2:3]参加物
実験手順
2-methacrylamidoethyl alcohol was prepared in substantially the same manner as in Example 11 except that 6.9 g of methacrylic acid and 16.5 g of dicyclohexylcarbodiimide and 4.9 g of ethanolamine were used. Subsequently, a polymer powder was obtained in substantially the same manner as in Example 11 except that 52.0 g of 2-methacryloyloxyethyl alcohol was used. The obtained polymer powder is referred to as "1T-40". Separately, 2-methacrylamidoethyl alcohol was prepared in substantially the same manner as in Example 11 except that 27.6 g of methacrylic acid and 66.0 g of dicyclohexylcarbodiimide and 19.6 g of ethanolamine were used. Subsequently, a polymer powder was obtained in substantially the same manner as in Example 11 except that 20.8 g of 2-methacryloyloxyethyl alcohol was used. The polymer powder is referred to as "4T-40".
出典と根拠
- ORDレコード
- ord-2d73f412f01f4f82bfeca3d2471c5f6d
- 出典データセット
- uspto-grants-1995_03
- 特許番号
- US05397682
関連ノート
読み込み中…