[CH2:1]=[CH:2][C:3]1[CH:8]=[CH:7][CH:6]=[CH:5][CH:4]=1.C([Li])CCC.C=CC(=C)C>C1CCCCC1.O1CCCC1>[CH2:1]=[CH:2][C:3](=[CH2:4])[CH3:8].[CH2:1]=[CH:2][C:3]1[CH:8]=[CH:7][CH:6]=[CH:5][CH:4]=1[CH2:1]=[CH:2][C:3]1[CH:8]=[CH:7][CH:6]=[CH:5][CH:4]=1.C([Li])CCC.C=CC(=C)C>C1CCCCC1.O1CCCC1>[CH2:1]=[CH:2][C:3](=[CH2:4])[CH3:8].[CH2:1]=[CH:2][C:3]1[CH:8]=[CH:7][CH:6]=[CH:5][CH:4]=1In a solution of styrene (41 g) in cyclohexane (1100 g), 0.3 ml of tetrahydrofuran and 1.2 g of 15 wt % n-butyllithium solution were added to initiate polymerization. The reaction was continued for 30 minutes, and the temperature was increased from 40° C. to 50° C. After most of the styrene monomer was reacted, 123 g of isoprene solution was added into the polymer mixture. The reaction was continued for an additional 90 minutes, and the temperature was increased from 55° C. to 80-90° C. After all of the isoprene monomer was completely reacted, a living styrene-isoprene block copolymer was formed in the first step.