Propylene Oxide → Acryloylglycine

HRID 37315

反応式

HRID 37315 の反応式
[OH-].[K+].C1OC1C.[NH:7]1[CH:11]([C:12]([O-:14])=[O:13])[CH2:10][CH2:9][C:8]1=[O:15].[Na+]>O>[C:12]([CH2:11][NH:7][C:8](=[O:15])[CH:9]=[CH2:10])([OH:14])=[O:13]

参加物

5

反応物 3

HCID 6378Propylene OxideHCID 14797Potassium HydroxideHCID 23666346Sodium Pyrrolidone Carboxylate

生成物 1

HCID 100321Acryloylglycine収率 292.6%

試薬・触媒・溶媒 1

HCID 962Water溶媒

実験手順

100 g of 25 wt % polyacrylic acid aqueous solution and 2.5 g of N-carboxy methyl acrylamide were polymerized at 60° C. for 3 hours for partial crosslinking. Potassium hydroxide was added to neutralize the pH value to 7.0 and 40 g of T-P400(polymer of triol and propylene oxide, Union Carbide Co., U.S.A.) and 1 g of sodium 2-pyrrolidone-5-carboxylate were added. Deionized water was then added to the resultant product to adjust the solid content thereof to 35 wt %. The viscosity of the resultant solution was measured as 5500 to 6000 cps(30° C.). The resulting product was tested according to the procedures set forth in Example 1, and the test results are listed in Table 1.

後処理

  1. customwas measured as 5500 to 6000 cps(30° C.)
  2. customthe test results