反応式
[C:1](#[N:4])[CH:2]=[CH2:3].[CH2:5]=[CH:6][C:7]1[CH:12]=[CH:11][CH:10]=[CH:9][CH:8]=1>>[CH2:5]=[CH:6][CH:7]=[CH2:8].[CH2:5]=[CH:6][C:7]1[CH:12]=[CH:11][CH:10]=[CH:9][CH:8]=1.[C:1](#[N:4])[CH:2]=[CH2:3]参加物
3
実験手順
The procedure of Example i was repeated except a total of 273 grams of acrylonitrile was used instead of the total of 546 grams as per Example 1. In this example, the incremental addition was repeated except only one half of each amount of acrylonitrile was used. A portion of the latex was isolated for subsequent blending and the remaining latex coagulated as per Example 1. The dry rubber had a Mooney viscosity (100° C.) of 127, a bound acrylonitrile content of 3.8 weight percent (by Carlo Erba nitrogen analysis), a bound styrene content of 40.4 weight percent (by FTIR analysis) and a glass transition temperature of -28° C. (by DSC, Differential Scanning Calorimetry).
後処理
- customA portion of the latex was isolated for subsequent blending
出典と根拠
- ORDレコード
- ord-5bb327bb0c724325a400c352678e7fb0
- 出典データセット
- uspto-grants-1993_07
- 特許番号
- US05225479
関連ノート
読み込み中…