Oxygen → Silica

Oxygen cleaning agent according to the invention was made as follows: a highly concentrated sodium silicate solution was prepared by reacting 45.4 kilograms of 99.9% silicic acid with 93.0 kilograms of 50% sodium hydroxide solution at 104.4° C. to 126.7° C. This temperature was maintained for four hours under reflux conditions not allowing the temperature to exceed 126.7° C. This material was then quenched with 68.0 kilograms of ASTM D1193 Type 1 demineralized water. Two hundred and twenty five grams of this 44% active polysilicate anion sodium silicate solution was mixed with one liter of ASTM D1193 Type 1 demineralized water to obtain a silicon dioxide:disodium oxide mole ratio of 1.83, a polysilicate anion concentration of 9.5% by weight and a pH of 12.4. This solution was then heated to 82.2° C. for two hours and filtered in steps through 50 micron, 10 micron and 3 micron filters. The solution was allowed to cool to room temperature, and five grams of 99.9% sodium molybdate was added as a corrosion inhibitor. Then 15 grams of 48 to 50% fluoroboric acid was added as an additional corrosion inhibitor reducing the pH to 11.93 and forming in situ sodium fluoroborate.

1. customat 104.4° C. to 126.7° C
2. temperatureThis temperature was maintained for four hours under reflux conditions not
3. customto exceed 126.7° C
4. customThis material was then quenched with 68.0 kilograms of ASTM D1193 Type 1 demineralized water
5. additionTwo hundred and twenty five grams of this 44% active polysilicate anion sodium silicate solution was mixed with one liter of ASTM D1193 Type 1 demineralized water

ORD 기록

ord-8847c530e1c54cc3bf0dabe2acfb6bf3

출처 데이터셋

uspto-grants-1995_06

DOI

10.6084/m9.figshare.5104873.v1

특허 번호

US05427709