Methanol → Trimethylsilylmethyl acrylate t-butyl methacrylate

HRID 341727

반응식

HRID 341727 반응식
[C:1]([O:6][C:7]([CH3:10])([CH3:9])[CH3:8])(=[O:5])[C:2]([CH3:4])=[CH2:3].[C:11]([O:15][CH2:16][Si:17]([CH3:20])([CH3:19])[CH3:18])(=[O:14])[CH:12]=[CH2:13].CC(N=NC(C#N)(C)C)(C#N)C.CO>C1(C)C=CC=CC=1.O>[C:11]([O:15][CH2:16][Si:17]([CH3:20])([CH3:19])[CH3:18])(=[O:14])[CH:12]=[CH2:13].[C:1]([O:6][C:7]([CH3:10])([CH3:9])[CH3:8])(=[O:5])[C:2]([CH3:4])=[CH2:3]

참가 물질

7

반응물 4

HCID 887MethanolHCID 6547AzobisisobutyronitrileHCID 11448tert-Butyl methacrylateHCID 15374992(Trimethylsilyl)methyl prop-2-enoate

생성물 1

HCID 86753515Trimethylsilylmethyl acrylate t-butyl methacrylate수율 85%

시약·촉매·용매 2

HCID 962Water용매HCID 1140Toluene용매3회

실험 절차

t-butyl methacrylate and trimethylsilylmethyl acrylate were mixed at a mixing ratio of 1:1 so as to form a toluene solution having a monomer concentration of 5 mol/liter. Next, 2 mol %, on the basis of the monomer, of AIBN was added to the mixture, and the mixture was retained in an oil bath at 80° C. for 3 hours with stirring. Thereafter, the mixture was left standing at room temperature to cool, and the reaction product was diluted with toluene. The toluene solution was dropped into large quantities of a mixed solvent of methanol and water having a mixing ratio of 1:1, and the resulting precipitate was filtered and dried to obtain a trimethylsilylmethyl acrylate/t-butyl methacrylate copolymer represented by the following formula, at a yield of 85%. The molecular weight was 23,000 and the dispersion was 1.63. ##STR17## wherein each of m and n is a positive integer.

후처리

  1. waitThereafter, the mixture was left
  2. customstanding at room temperature
  3. temperatureto cool
  4. filtrationthe resulting precipitate was filtered
  5. customdried