Phosphoric Acid → Zirconium phosphate

HRID 400319

반응식

HRID 400319 반응식
[OH-].[Zr+4:2].[OH-].[OH-].[OH-].[Zr].[P:7](=[O:11])([OH:10])([OH:9])[OH:8].[P]>O>[P:7]([O-:11])([O-:10])([O-:9])=[O:8].[Zr+4:2].[P:7]([O-:11])([O-:10])([O-:9])=[O:8].[P:7]([O-:11])([O-:10])([O-:9])=[O:8].[P:7]([O-:11])([O-:10])([O-:9])=[O:8].[Zr+4:2].[Zr+4:2]

참가 물질

6

반응물 4

HCID 1004Phosphoric AcidHCID 23995ZirconiumHCID 84465Zirconium hydroxide (Zr(OH)4), (T-4)-HCID 5462309Phosphorus

생성물 1

HCID 160986Zirconium phosphate

시약·촉매·용매 1

HCID 962Water용매

반응 조건

온도
80 °C

실험 절차

Catalyst preparation. A zirconium phosphate based catalyst was prepared by a co-precipitation method. A solution of zirconium hydroxide (Zr(OH)4) as a zirconium precursor was dissolved in deionized water. To this solution, a stoichiometric amount of phosphoric acid as a phosphorus precursor was added. The resulting mixture was heated at 80° C. for 2 hours to remove water, and a paste was obtained. The resulting paste was then dried in an oven at 100° C. overnight (about 12-18 hours) to remove the bulk of any remaining water, and to provide a powder. The powder was then calcined at 350° C. for 2 hours to obtain powdered zirconium phosphate.

후처리

  1. customCatalyst preparation
  2. customA zirconium phosphate based catalyst was prepared by a co-precipitation method
  3. customto remove water
  4. customa paste was obtained
  5. customThe resulting paste was then dried in an oven at 100° C. overnight (about 12-18 hours)
  6. customto remove the bulk of any remaining water
  7. customto provide a powder

출처 및 근거

ORD 기록
ord-5158bc0245e144c6ba10bfddbe185877
출처 데이터셋
uspto-grants-2014_06
특허 번호
US08741258B2