Ethylene Oxide → Benzene, ethenyl-, polymer with 1,3-butadiene

HRID 840338

반응식

HRID 840338 반응식
[CH2:1]=[CH:2][C:3]1C=CC=C[CH:4]=1.C=CC=C.C(O)(=O)C=C.CCCC[CH2:22][CH2:23][CH2:24][CH2:25][CH2:26][CH2:27][CH2:28][CH2:29]OCCOS(O)(=O)=O.N.C1OC1.[OH-].[Na+].[O-]S(OOS([O-])(=O)=O)(=O)=O.[Na+].[Na+]>O>[CH2:1]=[CH:2][CH:3]=[CH2:4].[CH2:29]=[CH:28][C:27]1[CH:22]=[CH:23][CH:24]=[CH:25][CH:26]=1

참가 물질

9

반응물 7

HCID 6354Ethylene OxideHCID 6581Acrylic Acid2회HCID 7501Styrene3회HCID 78451,3-ButadieneHCID 14798Sodium HydroxideHCID 61913Ammonium Laureth SulfateHCID 62655Sodium Persulfate

생성물 1

HCID 62697Benzene, ethenyl-, polymer with 1,3-butadiene

시약·촉매·용매 1

HCID 962Water용매3회

반응 조건

온도
68 °C

실험 절차

A styrene-butadiene dispersion was prepared by free-radical polymerization from 6 kg of styrene, 8.4 kg of 1,3-butadiene, 3.6 kg of acrylic acid, 0.41 kg of styrene seed latex dispersion (34% by weight in water, particle size about 30 to 35 nm), 135 g of Texapon® NSO solution (sodium lauryl ether sulfate having on average 2.5 ethylene oxide units; 28% strength by weight in water), 150 g of sodium hydroxide solution (10% strength by weight in water), 110 g of sodium peroxodisulfate and 18.28 kg of water at 82° C. Excess 1,3-butadiene was removed by injecting 2 bar of nitrogen with stirring into the dispersion, which had been cooled to 68° C., releasing the pressure and applying a slight underpressure (750 mbar absolute) and repeating this procedure in automated form about 1500 times. After 4 hours, a dispersion was obtained which had a solids content of 51.3% by weight, a pH of 4.8, and residual monomer contents of 1669 ppm of styrene and 280 ppm of acrylic acid.

후처리

  1. customExcess 1,3-butadiene was removed
  2. customa dispersion was obtained which

출처 및 근거

ORD 기록
ord-592cb45bc34a445bbdee2c4822c18c2b
출처 데이터셋
uspto-grants-2002_04
특허 번호
US06365709B1