Into a 500 ml-volume three-neck flask, 38.0 g (0.24 mol) of 1-ethoxyethyl methacrylate, 21.3 g (0.15 mol) of glycidyl methacrylate, 26.4 g (0.15 mol) of benzyl methacrylate, 5.2 g (0.06 mol) of methacrylic acid and 300 ml of methyl isobutyl ketone were charged. A catalytic amount of 2,2′-azobis(methyl 2-methylpropionate) was added thereto as a radical polymerization initiator, and polymerization was allowed to proceed at 80° C. for 6 hours in a nitrogen stream. The reaction solution was cooled and then poured in a large amount of heptane to precipitate a polymer. The crystal was collected by filtration and dissolved in a mixed solvent of propylene glycol monomethyl ether acetate and diethylene glycol ethyl methyl ether, and heptane and methyl isobutyl ketone contained in the solution were removed by distillation under reduced pressure to obtain Polymer A-7 (1-ethoxyethyl methacrylate/glycidyl methacrylate/benzyl methacrylate/methacrylic acid) as a solution in a mixed solvent of propylene glycol monomethyl ether acetate and diethylene glycol ethyl methyl ether.

1. customas a radical polymerization initiator, and polymerization
2. temperatureThe reaction solution was cooled
3. customto precipitate a polymer
4. filtrationThe crystal was collected by filtration
5. dissolutiondissolved in a mixed solvent of propylene glycol monomethyl ether acetate and diethylene glycol ethyl methyl ether, and heptane and methyl isobutyl ketone
6. customwere removed by distillation under reduced pressure