反应详情

温度

50 °C

To a stirred mixture of 9,9-dioctyl 2,7-fluorenediboronate (27.42 g, 51.2 mmol), 2,7-dibromo-9,9-dioctylfluorene (27.43 g, 50 mmol) in toluene (450 mL) under nitrogen are added sequentially the phase transfer catalyst, Aliquat® 336 (1.4 g, 3.4 mmol), tetrakis(triphenylphosphine)palladium (38 mg, 0.032 mmol), and 2M aqueous sodium carbonate (80 mL, 160 mmol). The mixture is stirred and heated under gentle reflux for 20 hours when a viscous reaction mixture is observed. One gram of bromobenzene is added and stirring and heating continued for 5 hours. The reaction mixture is cooled to about 50° C., added slowly to a vigorously stirred mixture of 3.5 L of methanol and 200 mL of 1N aqueous HCl. The polymer fibers are collected by filtration, washed successively with methanol (1 L), deionized water (500 mL), and methanol (1 L), and dried in a vacuum oven at 60° C. for 16 hours. The polymer weighed 39 g (100% yield). The inherent viscosity of the polymer is found to be 1.65 dL/g (THF, 25° C., 0.5 g/dL). The polymer is purified further by passing a toluene solution of the polymer through a column of silica gel and re-precipitation from 4 L of methanol. The purified polymer weighs 37 g (95% yield).

1. temperatureheated
2. temperatureunder gentle reflux for 20 hours when a viscous reaction mixture
3. stirringstirring
4. temperatureheating
5. filtrationThe polymer fibers are collected by filtration
6. washwashed successively with methanol (1 L), deionized water (500 mL), and methanol (1 L)
7. customdried in a vacuum oven at 60° C. for 16 hours
8. custom1.65 dL/g (THF, 25° C., 0.5 g/dL)
9. customThe polymer is purified further
10. customthrough a column of silica gel and re-precipitation from 4 L of methanol