C[Si](OC)(OC)OC.[Sb:9](=[O:13])([O-:12])([O-:11])[O-:10].[Zn+2:14].[Sb:15](=[O:19])([O-:18])([O-:17])[O-:16].[Zn+2].[Zn+2].[CH:22]([OH:25])([CH3:24])[CH3:23]>CO>[CH:22]([OH:25])([CH3:24])[CH3:23].[Sb:9](=[O:10])([O-:13])([O-:12])[O-:11].[Zn+2:14].[Sb:15](=[O:16])([O-:19])([O-:18])[O-:17].[Zn+2:14].[Zn+2:14]

Participants

5

Reactant 3

HCID 3776IsopropanolHCID 14456MethyltrimethoxysilaneHCID 21863617HCID 21863617, compound

Product 1

HCID 86755560HCID 86755560, compound

Reagents, catalysts & solvents 1

HCID 887MethanolSolvent

Procedure

To 769 g of the anhydrous zinc antimonate aqueous sol was added 2.81 g of methyltrimethoxysilane (manufactured by Toray Dow Corning Silicone Co., Ltd., trade name SZ6070) and the mixture was stirred at room temperature for 4 hours with a disper. To this were added 0.34 g of diisopropylamine and 0.80 g of malic acid, followed by mixing with stirring at room temperature for 2 hours with a disper. Thus, there was obtained a colloid solution of anhydrous zinc antimonate having the surface of whose particles was coated with methyltrimethoxysilane or its hydrolysate. The colloid solution had a pH of 3.4. The aqueous solvent of the surface-modified anhydrous zinc antimonate colloid solution was substituted by a methanol solvent and then by an isopropyl alcohol solvent using a rotary evaporator to produce surface-modified anhydrous zinc antimonate isopropyl alcohol sol. The resulting isopropyl alcohol sol contained 20.5% of ZnO.Sb2O5 and the amount of silane coupling agent coated was 0.7% by weight in terms of SiO2 based on the weight of ZnO.Sb2O5. The solution obtained by mixing this sol with water in a weight ratio of 1:1 had a pH of 4.3, and a primary particle diameter of 15 to 50 nm by transmission electron microscopic observation and aggregated particle size of 200 nm by laser scattering particle size distribution analyzer. A dry product of the sol had a volume resistivity of 1,762 Ω·cm.

Workup

  1. customa rotary evaporator