反应详情

51.1 g of acrylic acid was diluted with 22.6 g of water and neutralized with 75.0 g of a 30 wt. % aqueous sodium hydroxide solution under cooling. Thereafter, 143.3 of a 40 wt. % aqueous sodium acrylamidomethylpropanesulfonate solution was added thereto, and then 7.9 g of a 5.2 wt. % aqueous potassium persulfate solution and 0.082 g of epoxy bifunctional cross linking agent (ethylene glycol diglycidyl ether) were added thereto to prepare a homogeneous solution as the aqueous monomer/initiator solution. Thereafter, the same procedure as that of Example 18 was repeated, thereby providing 131.5 g of a sodium acrylate/sodium acrylamidomethylpropanesulfonate copolymer. The resultant polymer was in the form of distorted granular particles having an average diameter of 580 μm and a bulk density of 0.44 g/ml. The measurement was conducted on the resultant polymer particles in the same manner as that of Example 4. The results are given in Table 2.

1. temperatureunder cooling
2. additionwere added
3. customto prepare a homogeneous solution as the aqueous monomer/initiator solution