We have found that the presence of specific additives, not generally recognised as brighteners, in 2:1 chromium (III) chloride hexahydrate-choline chloride can significantly brighten the electrodeposit. For example when 10% of choline chloride is replaced by tetraethylammonium fluoride dihydrate or tetramethylammonium hydroxide pentahydrate thin semi-bright pale blue chromium deposits can be obtained. Approximately 6 ml of 2:1 chromium (III) chloride hexahydrate-[choline chloride (90%) tetraethylammonium fluoride dihydrate (10%)] was prepared by combining the reactants in a beaker and heating at 80° C. The green liquid was poured into an electrochemical cell (internal diameter of 23 mm) held in an oil bath at 60° C. Mild steel (50 mm by 10 mm and 1 mm thick), cleaned in the usual way, was fixed to the inside edge of the cell opposite a nickel counter electrode. The mild steel plate and counter-electrode were then connected to the negative and positive terminals respectively of a Thurlby Thander power pack. Using current densities between 8 and 16 mAcm−2 and deposition times between 10 and 30 minutes semi-bright chromium deposits were obtained. The procedure was repeated using approximately 6 ml of 2:1 chromium (III) chloride hexahydrate-[choline chloride (90%) tetramethylammonium hydroxide pentahydrate (10%)]. With a current density of 2 mAcm−2 thin pale blue semi-bright homogenous chromium deposits were obtained after 30 minutes.

1. customcan be obtained
2. additionThe green liquid was poured into an electrochemical cell (internal diameter of 23 mm)
3. customheld in an oil bath at 60° C