A glass ampule having a volume of 75 mL was charged with 50 g (0.25 mol) of diisopropyl fumarate, 1.9 g (0.013 mol) of cinnamic acid and 0.29 g (0.0016 mol) of tert-butyl peroxypivalate as a polymerization initiator and after repeating purging with nitrogen and release of the pressure, sealed in the pressure-reduced state. This ampule was placed in a constant temperature bath at 50° C. and held for 48 hours, thereby performing radical polymerization. After the completion of polymerization reaction, the polymerization product was taken out of the ampule and dissolved in 400 g of tetrahydrofuran. The resulting polymer solution was added dropwise, for precipitation, to 3 L of methanol, and the precipitate was vacuum-dried at 80° C. for 10 hours to obtain 21 g of a diisopropyl fumarate/cinnamic acid copolymer (yield: 41%).

1. customafter repeating purging with nitrogen and release of the pressure
2. customsealed in the pressure-reduced state
3. customThis ampule was placed in a constant temperature bath at 50° C.
4. custompolymerization
5. customAfter the completion of polymerization reaction
6. customthe precipitate was vacuum-dried at 80° C. for 10 hours