Lithium sulfide (Li2S) and phosphorus sulfide (P2S5) were used as the material composition, and lithium fluoride (LiF) was used as the fluoride. The powder of them was placed in a glove box in an atmosphere of argon, and 0.3828 g Li2S, 0.6172 g P2S5 and 0.01 g LiF were weighed and then these were mixed in an agate mortar. At this time, the ratio of Li2S and P2S5 was 75:25 on a molar basis. In addition, the amount of LiF added was 6.5 mole percent on a fluorine basis with respect to the solid electrolyte material to be obtained. Subsequently, the mixed composition was put into a 45 ml zirconia pot, zirconia balls were further put into the pot and then the pot was completely hermetically sealed. The pot was mounted on a planetary ball milling machine. Then, mechanical milling was performed at a rotational speed of 370 rpm for 40 hours. After that, the solid electrolyte material (Li2S—P2S5-based solid electrolyte material that contains fluorine) was obtained.

1. additionthese were mixed in an agate mortar
2. customto be obtained
3. custompot was completely hermetically sealed