Acrylic Acid → Phenoxyethyl acrylate methyl methacrylate acrylic acid

HRID 1473704

Reaktionsgleichung

Reaktionsgleichung von HRID 1473704
[C:1]([O:5][CH2:6][CH2:7][O:8][C:9]1[CH:14]=[CH:13][CH:12]=[CH:11][CH:10]=1)(=[O:4])[CH:2]=[CH2:3].[C:15]([O:20][CH3:21])(=[O:19])[C:16]([CH3:18])=[CH2:17].[C:22]([OH:26])(=[O:25])[CH:23]=[CH2:24].N(C(C)(C)C(OC)=O)=NC(C)(C)C(OC)=O>C(C(C)=O)C.C(O)(C)C>[C:1]([O:5][CH2:6][CH2:7][O:8][C:9]1[CH:10]=[CH:11][CH:12]=[CH:13][CH:14]=1)(=[O:4])[CH:2]=[CH2:3].[C:15]([O:20][CH3:21])(=[O:19])[C:16]([CH3:18])=[CH2:17].[C:22]([OH:26])(=[O:25])[CH:23]=[CH2:24]

Komponenten

7

Edukt 4

HCID 6581Acrylic AcidHCID 6658Methyl MethacrylateHCID 39485Phenoxyethyl acrylateHCID 757631,1'-Dimethyl 2,2'-(1,2-diazenediyl)bis(2-methylpropanoate)3×

Produkt 1

HCID 86634647Phenoxyethyl acrylate methyl methacrylate acrylic acid

Reagenzien, Katalysatoren, Lösungsmittel 2

HCID 3776IsopropanolLösungsmittelHCID 6569Methyl Ethyl KetoneLösungsmittel3×

Reaktionsbedingungen

Temperatur
75 °C

Versuchsvorschrift

360.0 g of methyl ethyl ketone was placed in a 2 L three-necked flask equipped with a stirrer, a thermometer, a reflux condenser, and a nitrogen gas introduction tube, and was heated to 75° C. Thereafter, while the temperature inside the flask was maintained at 75° C., a mixture solution of 180.0 g of phenoxyethyl acrylate, 162.0 g of methyl methacrylate, 18.0 g of acrylic acid, 72 g of methyl ethyl ketone, and 1.44 g of V-601 (trade name, manufactured by Wako Pure Chemical Industries Ltd.) was added dropwise into the flask at a constant rate such that the dropwise addition was completed in 2 hours. After the dropwise addition was completed, a solution of 0.72 g of V-601 in 36.0 g of methyl ethyl ketone was added into the flask, stirred at 75° C. for 2 hours, and a solution of 0.72 g of V-601 in 36.0 g of isopropanol was further added, and the contents of the flask were stirred at 75° C. for 2 hours. Then, the temperature was increased to 85° C., and stirring was continued for another 2 hours. As a result, a resin solution of a copolymer of phenoxyethyl acrylate/methyl methacrylate/acrylic acid (in a ratio of 50/45/5 by mass) was obtained.

Aufarbeitung

  1. customequipped with a stirrer
  2. temperatureThereafter, while the temperature inside the flask was maintained at 75° C.
  3. additionAfter the dropwise addition
  4. stirringthe contents of the flask were stirred at 75° C. for 2 hours
  5. temperatureThen, the temperature was increased to 85° C.
  6. stirringstirring
  7. waitwas continued for another 2 hours