Methacrylic Acid → Methacrylic acid ethylene oxide

HRID 491256

Reaktionsgleichung

Reaktionsgleichung von HRID 491256
[Na:1].[CH2:2]1[O:4][CH2:3]1.[C:5]([OH:10])(=[O:9])[C:6]([CH3:8])=[CH2:7].[CH2:11]=[CH:12][C:13]1[CH:18]=[CH:17][CH:16]=[CH:15][CH:14]=1.[C:19]([OH:24])(=[O:23])[C:20]([CH3:22])=[CH2:21].[C:25]([O:29][CH2:30][CH2:31][CH2:32][CH3:33])(=[O:28])[CH:26]=[CH2:27].S(OOS([O-])(=O)=O)([O-])(=O)=O.[NH4+].[NH4+]>O>[CH:11]([CH2:7][C:6](=[CH2:8])[C:5]([OH:10])=[O:9])=[CH:12][C:13]1[CH:18]=[CH:17][CH:16]=[CH:15][CH:14]=1.[C:25]([O:29][CH2:30][CH2:31][CH2:32][CH3:33])(=[O:28])[CH:26]=[CH2:27].[Na:1].[CH2:3]1[O:4][CH2:2]1.[C:19]([OH:24])(=[O:23])[C:20]([CH3:22])=[CH2:21]

Komponenten

9

Edukt 6

HCID 4093Methacrylic AcidHCID 7501StyreneHCID 8846Butyl AcrylateHCID 62648Ammonium Persulfate2×HCID 5360545SodiumHCID 21880491Methacrylic acid ethylene oxide

Produkt 2

HCID 21880491Methacrylic acid ethylene oxideHCID 86591398Styrene-methacrylic acid butyl acrylate sodium

Reagenzien, Katalysatoren, Lösungsmittel 1

HCID 962WaterLösungsmittel

Reaktionsbedingungen

Temperatur
75 °C

Versuchsvorschrift

683 parts of water, 11 parts of the sodium salt of the sulfuric acid ester of methacrylic acid ethylene oxide adduct (ELEMINOL RS-30, Sanyo Chemical Industries, Ltd.), 83 parts of styrene, 83 parts of methacrylic acid, 110 parts of butyl acrylate and 1 part of ammonium persulphate were introduced into a reaction vessel provided with a stirrer and thermometer, and stirred at 400 rpm/min for 15 minutes to give a white emulsion. This was heated, the temperature in the system was raised to 75° C. and the reaction performed for 5 hours. Next, 30 parts of an aqueous solution of 1% ammonium persulphate was added, and the reaction mixture matured and 75° C. for 5 hours to obtain an aqueous dispersion of a vinyl resin (copolymer of styrene-methacrylic acid-butyl acrylate-sodium salt of the sulfuric acid ester of methacrylic acid ethylene oxide adduct), “particulate emulsion 1.” The volume average particle diameter of particulate emulsion 1 measured by LA-920 was 105 nm. After drying part of “particulate emulsion 1” and isolating the resin, Tg of the resin was 59° C. and the volume average molecular weight was 150000.

Aufarbeitung

  1. customprovided with a stirrer
  2. customto give a white emulsion
  3. temperatureThis was heated
  4. waitthe reaction performed for 5 hours