Reaktionsgleichung
[C:1]1(=[O:7])O[C:4](=[O:5])[CH:3]=[CH:2]1.[CH2:8]([NH2:20])[CH2:9][CH2:10][CH2:11][CH2:12][CH2:13][CH2:14][CH2:15][CH2:16][CH2:17][CH2:18][CH3:19].P(=O)(O)(O)O.COC1C(=O)C=CC(=O)C=1>C1C2C(=CC=CC=2)CCC1.C([O-])(=O)C.[Zn+2].C([O-])(=O)C>[CH2:8]([N:20]1[C:4](=[O:5])[CH:3]=[CH:2][C:1]1=[O:7])[CH2:9][CH2:10][CH2:11][CH2:12][CH2:13][CH2:14][CH2:15][CH2:16][CH2:17][CH2:18][CH3:19]Komponenten
Edukt 4
Produkt 1
Reagenzien, Katalysatoren, Lösungsmittel 2
Reaktionsbedingungen
- Temperatur
- 210 °C
Versuchsvorschrift
The same reactor as used in Example 7 was adopted. In this reactor, a solution of 120 g of maleic anhydride in 360 g of tetrahydronaphthalene was placed. Then, a solution of 220 g of dodecylamine and 1760 g of tetrahydronaphthalene was added thereto at 40° C. over a period of 120 minutes. After the addition was completed, the resultant mixture and 65.4 g of ortho-phosphoric acid (purity 89% by weight), 1.344 g of methoxybenzoquinone, and 0.1 g of zinc acetate added thereto were heated at 210° C. for one hour to effect reaction. Thereafter, the resultant reaction mixture was cooled to 30° C. and separated into a water layer and a tetrahydronaphthalene layer. The tetrahydronaphthalene layer was distilled to expel tetrahydronaphthalene. Consequently, there was obtained 285 g of slightly impure N-dodecyl maleimide. It was found to have purity of 92.3% by weight, indicating the yield thereof to be 83.5 mol % based on dodecylamine.
Aufarbeitung
- additionAfter the addition
- customreaction
- customThereafter, the resultant reaction mixture
- temperaturewas cooled to 30° C.
- customseparated into a water layer
- distillationThe tetrahydronaphthalene layer was distilled
Quellen und Nachweise
- ORD-Eintrag
- ord-a656e95f3f9749a89d4dce64cc03a074
- Quelldatensatz
- uspto-grants-1988_10
- Patentnummer
- US04780546