Glycidyl acrylate → 1-Ethoxy-2-(2-methoxyethoxy)ethane

HRID 1425623

反応式

HRID 1425623 の反応式
[C:1]([O:6][CH:7]([O:9][CH2:10][C:11]1[CH:16]=[CH:15][CH:14]=[CH:13][CH:12]=1)[CH3:8])(=[O:5])[C:2]([CH3:4])=[CH2:3].[C:17]([O:21][CH2:22][CH:23]1[O:25][CH2:24]1)(=[O:20])[CH:18]=[CH2:19].[C:26]([O:31][CH2:32][CH2:33][OH:34])(=[O:30])[C:27]([CH3:29])=[CH2:28].N([C:44](C)(CC)[C:45]([O-:47])=O)=NC(C)(CC)C([O-])=O>CCCCCCC.C(C(C)=O)C(C)C>[C:1]([O:6][CH:7]([O:9][CH2:10][C:11]1[CH:12]=[CH:13][CH:14]=[CH:15][CH:16]=1)[CH3:8])(=[O:5])[C:2]([CH3:4])=[CH2:3].[C:17]([O:21][CH2:22][CH:23]1[O:25][CH2:24]1)(=[O:20])[CH:18]=[CH2:19].[C:26]([O:31][CH2:32][CH2:33][OH:34])(=[O:30])[C:27]([CH3:29])=[CH2:28].[CH3:24][O:25][CH2:23][CH2:22][O:21][CH2:17][CH2:18][O:47][CH2:45][CH3:44]

参加物

8

反応物 4

HCID 7836Glycidyl acrylateHCID 133602-Hydroxyethyl MethacrylateHCID 218349871-Benzyloxyethyl methacrylateHCID 219175032,2'-Azobis(methyl 2-methylpropanate)

生成物 2

HCID 138471-Ethoxy-2-(2-methoxyethoxy)ethaneHCID 866432081-Benzyloxyethyl methacrylate glycidyl acrylate 2-hydroxyethyl methacrylate

試薬・触媒・溶媒 2

HCID 7909Methyl Isobutyl Ketone溶媒HCID 8900Heptane溶媒

実験手順

Into a 500 ml-volume three-neck flask, 79.3 g (0.36 mol) of 1-benzyloxyethyl methacrylate, 23.1 g (0.18 mol) of glycidyl acrylate, 7.8 g (0.06 mol) of 2-hydroxyethyl methacrylate and 300 ml of methyl isobutyl ketone were charged. A catalytic amount of 2,2′-azobis(methyl 2-methylpropionate) was added thereto as a radical polymerization initiator, and polymerization was allowed to proceed at 80° C. for 6 hours in a nitrogen stream. The reaction solution was cooled and then poured in a large amount of heptane to precipitate a polymer. The crystal was collected by filtration and dissolved in diethylene glycol ethyl methyl ether, and heptane and methyl isobutyl ketone contained in the solution were removed by distillation under reduced pressure to obtain Polymer A-3 (1-benzyloxyethyl methacrylate/glycidyl acrylate/2-hydroxyethyl methacrylate) as a diethylene glycol ethyl methyl ether solution.

後処理

  1. customas a radical polymerization initiator, and polymerization
  2. temperatureThe reaction solution was cooled
  3. customto precipitate a polymer
  4. filtrationThe crystal was collected by filtration
  5. dissolutiondissolved in diethylene glycol ethyl methyl ether
  6. customwere removed by distillation under reduced pressure