Glycidyl methacrylate → 1-Ethoxy-2-(2-methoxyethoxy)ethane

HRID 1618841

反応式

HRID 1618841 の反応式
[C:1]([O:6][CH2:7][CH:8]1[O:10][CH2:9]1)(=[O:5])[C:2]([CH3:4])=[CH2:3].[C:11]([O:16][CH:17]([O:19][CH2:20][CH3:21])[CH3:18])(=[O:15])[C:12]([CH3:14])=[CH2:13].[C:22]([O:27][CH2:28][CH2:29][OH:30])(=[O:26])[C:23]([CH3:25])=[CH2:24].[C:31]([O:36][CH2:37][C:38]1[CH:43]=[CH:42][CH:41]=[CH:40][CH:39]=1)(=[O:35])[C:32]([CH3:34])=[CH2:33].N(C(C)(CC)C([O-])=O)=NC(C)(CC)C([O-])=O>CCCCCCC.C(C(C)=O)C(C)C>[CH3:1][O:6][CH2:7][CH2:8][O:10][CH2:21][CH2:20][O:19][CH2:17][CH3:18].[C:1]([O:6][CH2:7][CH:8]1[O:10][CH2:9]1)(=[O:5])[C:2]([CH3:4])=[CH2:3].[C:11]([O:16][CH:17]([O:19][CH2:20][CH3:21])[CH3:18])(=[O:15])[C:12]([CH3:14])=[CH2:13].[C:22]([O:27][CH2:28][CH2:29][OH:30])(=[O:26])[C:23]([CH3:25])=[CH2:24].[C:31]([O:36][CH2:37][C:38]1[CH:39]=[CH:40][CH:41]=[CH:42][CH:43]=1)(=[O:35])[C:32]([CH3:34])=[CH2:33]

参加物

9

反応物 5

HCID 7837Glycidyl methacrylateHCID 133602-Hydroxyethyl MethacrylateHCID 17236Benzyl methacrylateHCID 201933451-Ethoxyethyl Methacrylate (stabilized with MEHQ)HCID 219175032,2'-Azobis(methyl 2-methylpropanate)

生成物 2

HCID 138471-Ethoxy-2-(2-methoxyethoxy)ethaneHCID 86655549Glycidyl methacrylate 1-ethoxyethyl methacrylate 2-hydroxyethyl methacrylate benzyl methacrylate

試薬・触媒・溶媒 2

HCID 7909Methyl Isobutyl Ketone溶媒HCID 8900Heptane溶媒

実験手順

A 500 ml three-necked flask was charged with 34.1 g (0.24 mol) of glycidyl methacrylate, 28.5 g (0.18 mol) of 1-ethoxyethyl methacrylate, 7.8 g (0.06 mol) of 2-hydroxyethyl methacrylate, 21.1 g (0.12 mol) of benzyl methacrylate and 300 ml of methyl isobutyl ketone. A catalytic amount of 2,2′-azobis(methyl 2-methylpropionate) as a radical polymerization initiator was added to the mixture, and polymerization was performed in a nitrogen stream at 80° C. for six hours. The obtained reaction liquid was cooled, and poured in a large volume of heptane, thereby precipitating a polymer. The polymer crystal was collected by filtration, and dissolved in diethylene glycol ethyl methyl ether. The heptane and methyl isobutyl ketone contained in the solution were distilled off in vacuum, thereby obtaining a diethylene glycol ethyl methyl ether solution of polymer A2-6 (glycidyl methacrylate/1-ethoxyethyl methacrylate/2-hydroxyethyl methacrylate/benzyl methacrylate).

後処理

  1. customThe obtained reaction liquid
  2. temperaturewas cooled
  3. customprecipitating a polymer
  4. filtrationThe polymer crystal was collected by filtration
  5. dissolutiondissolved in diethylene glycol ethyl methyl ether
  6. distillationwere distilled off in vacuum