1-Butanol → HCID 178514811、化合物
反応式
[Ir:1].[Ta:2].C([OH:7])CCC>[Ti]>[Ir:1]=[O:7].[O-2:7].[Ta+5:2].[O-2:7].[O-2:7].[O-2:7].[O-2:7].[Ta+5:2]参加物
5
実験手順
After the roughened titanium substrate surface was heat treated, it was painted with a n-butanol solution containing salts of iridium and tantalum. The ratio of iridium to tantalum in the solution was about 65% to 35% by weight. The solution was allowed to dry at ambient temperature for approximately 20 minutes. The painted titanium substrate was subsequently heat treated in a furnace having an oxygen containing atmosphere at approximately 500° C. for approximately 20-30 minutes to form an iridium oxide/tantalum oxide composite coating. The process of painting and heat treating the titanium substrate was repeated to obtain a first layer having a total loading of 2.0 g/m2. After the desired loading was achieved, the anode was heat treated for approximately one hour at approximately 500° C.
後処理
- additiontreated
- customto dry at ambient temperature for approximately 20 minutes
- temperatureThe painted titanium substrate was subsequently heat
- additiontreated in a furnace
- customat approximately 500° C.
- customfor approximately 20-30 minutes