2-Hydroxyethyl Methacrylate → 1-Ethoxy-2-(2-methoxyethoxy)ethane

HRID 574020

反応式

HRID 574020 の反応式
[C:1]([O:6][CH:7]([O:9][CH2:10][CH3:11])[CH3:8])(=[O:5])[C:2]([CH3:4])=[CH2:3].[C:12]([O:17][CH2:18][C:19]1[CH:24]=[CH:23][CH:22]=[CH:21][CH:20]=1)(=[O:16])[C:13]([CH3:15])=[CH2:14].[C:25]([O:30][CH2:31][CH2:32][OH:33])(=[O:29])[C:26]([CH3:28])=[CH2:27].N(C(C)(CC)C([O-])=O)=NC(C)(CC)C([O-])=O>CCCCCCC.C(C(C)=O)C(C)C>[C:1]([O:6][CH:7]([O:9][CH2:10][CH3:11])[CH3:8])(=[O:5])[C:2]([CH3:4])=[CH2:3].[C:12]([O:17][CH2:18][C:19]1[CH:20]=[CH:21][CH:22]=[CH:23][CH:24]=1)(=[O:16])[C:13]([CH3:15])=[CH2:14].[C:25]([O:30][CH2:31][CH2:32][OH:33])(=[O:29])[C:26]([CH3:28])=[CH2:27].[CH3:25][O:30][CH2:31][CH2:32][O:33][CH2:11][CH2:10][O:9][CH2:7][CH3:8]

参加物

8

反応物 4

HCID 133602-Hydroxyethyl MethacrylateHCID 17236Benzyl methacrylateHCID 201933451-Ethoxyethyl Methacrylate (stabilized with MEHQ)HCID 219175032,2'-Azobis(methyl 2-methylpropanate)

生成物 2

HCID 138471-Ethoxy-2-(2-methoxyethoxy)ethaneHCID 673222671-Ethoxyethyl methacrylate benzyl methacrylate 2-hydroxyethyl methacrylate

試薬・触媒・溶媒 2

HCID 7909Methyl Isobutyl Ketone溶媒HCID 8900Heptane溶媒

実験手順

Into a 500 ml-volume three-neck flask, 66.4 g (0.42 mol) of 1-ethoxyethyl methacrylate, 21.1 g (0.12 mol) of benzyl methacrylate, 7.8 g (0.06 mol) of 2-hydroxyethyl methacrylate and 300 ml of methyl isobutyl ketone were charged. A catalytic amount of 2,2′-azobis(methyl 2-methylpropionate) was added thereto as a radical polymerization initiator, and polymerization was allowed to proceed at 80° C. for 6 hours in a nitrogen stream. The reaction solution was cooled and then poured in a large amount of heptane to precipitate a polymer. The crystal was collected by filtration and dissolved in diethylene glycol ethyl methyl ether, and heptane and methyl isobutyl ketone contained in the solution were removed by distillation under reduced pressure to obtain Polymer A1-3 (1-ethoxyethyl methacrylate/benzyl methacrylate/2-hydroxyethyl methacrylate) as a diethylene glycol ethyl methyl ether solution.

後処理

  1. customas a radical polymerization initiator, and polymerization
  2. temperatureThe reaction solution was cooled
  3. customto precipitate a polymer
  4. filtrationThe crystal was collected by filtration
  5. dissolutiondissolved in diethylene glycol ethyl methyl ether
  6. customwere removed by distillation under reduced pressure

出典と根拠

ORDレコード
ord-a8173f061ccd4c208b44f6df00abba57
出典データセット
uspto-grants-2015_05
特許番号
US09034440B2