反応式
[CH:1]1[C:6]([OH:7])=[CH:5][CH:4]=[CH:3][C:2]=1[CH3:8].[OH:9][CH2:10]C1C(O)=C(CO)C=C(C)C=1.O.O.C(O)(=O)C(O)=O.CCOCCOC(C)=O.C=O>O>[C:1]1([CH:10]=[O:9])[C:2]([CH3:8])=[CH:3][CH:4]=[CH:5][C:6]=1[OH:7]参加物
反応条件
- 温度
- 70 °C
実験手順
A phenolic resin rich in alternating phenolic copolymer block segments was formed by first reacting a mixture of 519.0 g of 99 percent pure m-cresol, 538.2 g 97 percent pure 2,6-bis(hydroxymethyl)-p-cresol and 20 g oxalic acid dihydrate in a solvent mixture of 40 ml deionized water and 200 ml ethyl cellosolve acetate. The reaction mixture was heated to about 70° C. to initiate the reaction forming the alternating copolymer. At 102° C., 32.6 g of 36.9 percent formaldehyde was added in 8 minutes to the reaction mixture to form substantially m-cresol-formaldehyde block segments and to chemically bond these segments to the previously formed alternating copolymer. After heating the mixture at reflux for three hours, the amount of heat was increased to remove the water and solvent by distillation. Partial vacuum was applied at about 220° C. and gradually increased to 4 mm Hg to remove the unreacted monomers. Maximum mixture temperature during vacuum stripping was about 226° C. The copolymer was poured from the reaction kettle and allowed to cool. About 840 g of a block copolymer resin having a number average molecular weight, Mn, of 1241 Daltons and a Tg of 112° C. were obtained.
後処理
- customwas formed
- additionin a solvent mixture of 40 ml
- customforming the alternating copolymer
出典と根拠
- ORDレコード
- ord-d7196dfa79ee47dd8dc4d11fe19bc97e
- 出典データセット
- uspto-grants-1992_07
- 特許番号
- US05130410
関連ノート
読み込み中…