20 g of N-vinylpyrrolidone and 2 g of N-vinylformamide were polymerized in 120 ml of water, to which 1 ml of NH4OH solution was added, at 80° C. under a blanket of argon. Initiator α,α'-azoisobutyronitrile 110 mg, polymerization time 24 h. 145 ml of concentrated hydrochloric acid were added to the resulting aqueous copolymer solution, and the mixture was refluxed (110° C.) for 7 h. The mixture was subsequently worked up as described in A using a strongly basic ion exchanger. 160 g of aqueous solution of an N-vinylamine/N-vinylpyrrolidone copolymer with an N-vinylamine content of 5.7% by weight were then obtained. The solids content of the polymer solution was 9.53%, the pH was 10.1, and the reduced viscosity of the polymer was determined as 1.61 dl/g (measured on a 1% strength solution in H2O at 25° C.).