Carbon Dioxide → Carbon Dioxide

Synthesis gas having an inlet composition of 66.6% H2, 33.3% CO and 0.1% CO2 was fed to a 300 cc. stainless steel autoclave charged with 3 gms. copper-chromite (containing 31.1% copper and 29% chromium), 1.2 gm. potassium formate and 150 cc. methanol, reduced in situ using a stream of pure H2 flowing at 25 cc/min. for 16 hours at 170° C. Both catalysts were added separately in the powder form. The reactor was pressurized to 910 psig. and the temperature was adjusted to 150° C. Synthesis gas at a flow rate of 105 cc/min. (measured under standard conditions) was made to react under isothermal conditions. After an initial transient period, the process reached a steady state with respect to the amount of synthesis gas converted. A methanol production rate based on H2 consumption of 17.16 gmoles/h/kg catalyst was obtained with 60% synthesis gas conversion and 95% selectivity towards methanol. An exit gas composition of 62% H2, 36% CO, 0.7% CO2, 0.6% methanol, 0.4% methyl formate, 0.1% H2O and 0.07% dimethyl ether was obtained. A liquid composition of 95.4% methanol, 4% methyl formate, 0.3% water and traces of dimethyl ether and dissolved gases was obtained.

1. customSynthesis gas
2. customfor 16 hours
3. customat 170° C
4. additionBoth catalysts were added separately in the powder form
5. customwas adjusted to 150° C
6. customSynthesis gas at a flow rate of 105 cc/min. (measured under standard conditions)
7. customto react under isothermal conditions
8. customto the amount of synthesis gas
9. customA methanol production rate based on H2 consumption of 17.16 gmoles/h/kg catalyst
10. customwas obtained with 60% synthesis gas conversion and 95% selectivity towards methanol