A heteroarm star polymer was prepared by stage polymerization using pentaerythritol tetrakis(3-mercaptopropionate). A monomer blend of 5 pphm vinyltriisoproxysilane, 5 pphm of butyl acrylate, 40 pphm of butyl methacrylate and 2.5 pphm of pentaerythritol tetrakis(3-menrcaptopropionate) was polymerized for 45 minutes with 0.5 pphm AIBN as catalyst. A second monomer mixture of 5 pphm of butyl acrylate, 5 pphm of vinyltriisopropoxysilane and 40 pphm of acrylic acid was then added to the reaction and the polymerization continued for 2 additional hours. The reaction was cooled and aqueous ammonium hydroxide was added and stirred for 30 minutes. After that, the isopropyl alcohol was removed and water was added to make a stable colloid. The end polymer pH was adjusted to 9.5 using aqueous ammonium hydroxide. The physical properties of the polymer are summarized in Table I.

1. customA heteroarm star polymer was prepared by stage polymerization
2. additionwas then added to the reaction
3. temperatureThe reaction was cooled
4. customAfter that, the isopropyl alcohol was removed
5. additionwater was added