5-hydroxy-1-naphthalenyl methacrylate (a.k.a. hydroxynaphthalene methacrylate or NAMA) monomer (2.60 g, 0.0045 mole), hexafluoroisopropyl methacrylate (iPrHFAMA) monomer (23.20 g, 0.0800 mole), 2-methacryloyl-gamma-butyrolactone (a.k.a. gamma-butyrolactone methacrylate or GBLMA) monomer (3.88 g, 0.0051 mole), azobisisobutyronitrile (AlBN) (0.91 g, 10% the total mole of all monomers), 150 g of tetrahydrofuran (THF) and 72 g of ethylacetate were added to a 250 ml 3-neck round bottom flask equipped with condenser, thermometer, nitrogen inlet and magnetic stirrer bar. The reaction mixture was stirred at room temperature and bubbled with N2 flow for 45 minutes after which is was heated to 67–70° C. and stirred for 14 hours with a blanket N2 flow. After reaction, the solution was then cooled to room temperature and added dropwise to 1200 g of hexane. The resulting slurry was stirred for two hours before filtration. Solid was air dried on the Buckner filter for 1.5 hours, dissolved in acetone (15% wt-wt) and reprecipitated in 1200 g of hexane. The slurry was again stirred for two hours before filtration. The solid was collected and air dried for 2–3 hours before final drying in a vacuum oven at 60° C. overnight. Yield: 90%.

1. customequipped with condenser
2. custombubbled with N2 flow for 45 minutes after which
3. temperatureis was heated to 67–70° C.
4. stirringstirred for 14 hours with a blanket N2 flow
5. customAfter reaction
6. temperaturethe solution was then cooled to room temperature
7. stirringThe resulting slurry was stirred for two hours before filtration
8. customdried on the Buckner
9. filtrationfilter for 1.5 hours
10. dissolutiondissolved in acetone (15% wt-wt)
11. customreprecipitated in 1200 g of hexane
12. stirringThe slurry was again stirred for two hours before filtration
13. customThe solid was collected
14. customair dried for 2–3 hours
15. custombefore final drying in a vacuum oven at 60° C. overnight