[C:1]([O:5][CH2:6][CH3:7])(=[O:4])[CH:2]=[CH2:3].[C:8](#[N:11])[CH:9]=[CH2:10].[C:12]([OH:16])(=[O:15])[CH:13]=[CH2:14].C(S)CCCCCCCCCCC.C(OOCCCCCCCCCCCC)CCCCCCCCCCC.C(OOC(=O)C1C=CC=CC=1)CCC>C1(C)C(C)=CC=CC=1>[CH2:6]([O:5][C:1](=[O:4])[CH:2]=[CH2:3])[CH3:7].[C:12]([OH:16])(=[O:15])[CH:13]=[CH2:14].[C:8](#[N:11])[CH:9]=[CH2:10]参加物
8
実験手順
this polymer material was produced by adding to 320 g xylene at 100° C. the monomer solution and a catalyst solution over a period of 3 hours. The monomer solution contained 2.900 g ethyl acrylate, 76 g acrylonitrile, 76 g acrylic acid and 3 g laurylmercaptan. The catalyst solution contained 26 g laurylperoxide and 7 g butylperbenzoate in 273 g of xylene. The material was highly viscous with comonomer proportions of 95:2.5:2.5.