Methacrylic Acid → Methacrylic Acid

HRID 2224005

反応式

HRID 2224005 の反応式
[Na:1].[CH2:2]1[O:4][CH2:3]1.[C:5]([OH:10])(=[O:9])[C:6]([CH3:8])=[CH2:7].[CH2:11]=[CH:12][C:13]1[CH:18]=[CH:17][CH:16]=[CH:15][CH:14]=1.[C:19]([O:23][CH2:24][CH2:25][CH2:26][CH3:27])(=[O:22])[CH:20]=[CH2:21].C(OCCCC)(=O)CS.S(OOS([O-])(=O)=O)([O-])(=O)=O.[NH4+].[NH4+]>O>[CH:11]([CH2:7][C:6](=[CH2:8])[C:5]([OH:10])=[O:9])=[CH:12][C:13]1[CH:18]=[CH:17][CH:16]=[CH:15][CH:14]=1.[C:19]([O:23][CH2:24][CH2:25][CH2:26][CH3:27])(=[O:22])[CH:20]=[CH2:21].[Na:1].[CH2:3]1[O:4][CH2:2]1.[C:5]([OH:10])(=[O:9])[C:6]([CH3:8])=[CH2:7]

参加物

11

反応物 7

HCID 4093Methacrylic Acid2 回HCID 6354Ethylene OxideHCID 7501StyreneHCID 8846Butyl AcrylateHCID 62648Ammonium Persulfate2 回HCID 82321Butyl ThioglycolateHCID 5360545Sodium

生成物 3

HCID 4093Methacrylic AcidHCID 6354Ethylene OxideHCID 86591398Styrene-methacrylic acid butyl acrylate sodium

試薬・触媒・溶媒 1

HCID 962Water溶媒

反応条件

温度
75 °C

実験手順

In a reactor equipped with a stirring rod and a thermometer were placed 683 parts of water, 11 parts of a sodium salt of sulfuric acid ester of ethylene oxide adduct of methacrylic acid ELEMINOL RS-30 (trade name, available from Sanyo Chemical Industries, Ltd.), 80 parts of styrene, 83 parts of methacrylic acid, 110 parts of butyl acrylate, 12 parts of butyl thioglycolate and 1 part of ammonium persulfate, and the mixture was stirred at 400 rpm for 15 minutes to yield a white emulsion. The emulsion was heated to an inner temperature of 75° C., followed by reaction for 5 hours. The reaction mixture was further treated with 30 parts of a 1% aqueous solution of ammonium persulfate, was aged at 75° C. for 5 hours and thereby yielded an aqueous dispersion [Fine Particle Dispersion 2] of a vinyl resin (a copolymer of styrene-methacrylic acid-butyl acrylate-sodium salt of sulfuric acid ester of ethylene oxide adduct of methacrylic acid). Fine Particle Dispersion 2 had a weight-average particle diameter of 120 nm as determined with a laser diffraction-scattering size distribution analyzer LA-920 (trade name, available from Horiba, Ltd.). Part of Fine Particle Dispersion 2 was dried to isolate a resin component. The resin component had a Tg of 42° C. and a weight-average molecular weight of 3×104.

後処理

  1. customIn a reactor equipped with a stirring rod
  2. customto yield a white emulsion
  3. customfollowed by reaction for 5 hours